J. Mater. Chem. C, 2022,10, 9841-9848.https://doi.org/10.1039/D2TC01672A

As an emerging material, organic–inorganic metal halides (OIMHs) have been widely studied in the field of optoelectronics in recent years. In this work, a series of compounds (TMEDA)₃(Sb_xBi_1−x)₂Cl₁₂·H₂O (0.1 ≤ x ≤ 0.6) (TMEDA = N,N,N′-trimethylethylenediamine) were synthesized. The incorporation of Sb³⁺ greatly enhanced the photoluminescence quantum yield of (TMEDA)₃Bi₂Cl₁₂·H₂O from 1% to 38%. The variation in the degree of distortion of the inorganic octahedra and the relatively suitable distances between metal ions are considered to be the reasons for the intense emission. (TMEDA)₃(Sb_xBi_1−x)₂Cl₁₂·H₂O (0.1 ≤ x ≤ 0.6) exhibited a yellow phosphorescence emission at 605 nm and 595 nm under excitation at 305 nm and 375 nm, respectively. With the incorporation of Sb³⁺, changes in the emission intensity under different excitation wavelengths showed different trends. Thus, we attribute the yellow broadband emissions to the triplet emission of Bi³⁺ and Sb³⁺. Finally, we combined (TMEDA)₃(Sb_0.5Bi_0.5)₂Cl₁₂·H₂O with commercial phosphors and a near-ultraviolet light-emitting diode chip to prepare a white-light-emitting diode device, which exhibited a high color-rendering index of 94.4. The aim of our work was to investigate the structural effects of the photoluminescence of Sb³⁺-doped OIMHs and to further explore ways to improve the Sb³⁺ emission efficiency in the field of photoluminescence of OIMHs.