Efficiency-Tunable Single-Component White-Light Emission Realized in Hybrid Halides Through Metal Co-Occupation

ACS Appl. Mater. Interfaces 2021, 13, 25, 29835–29842 https://pubs.acs.org/doi/abs/10.1021/acsami.1c07636

Organic–inorganic hybrid metal halides have attracted widespread attention as emerging optoelectronic materials, especially in solid-state lighting, where they can be used as single-component white-light phosphors for white light-emitting diodes. Herein, we have successfully synthesized a zero-dimensional (0D) organic–inorganic hybrid mixed-metal halide (Bmpip)2PbxSn1–xBr4 (0 < x < 1, Bmpip+ = 1-butyl-1-methyl-piperidinium, C10H22N+) that crystallizes in a monoclinic system in the C2/c space group. Pb2+ and Sn2+ form a four-coordinate seesaw structure separated by organic cations forming a 0D structure. For different excitation wavelengths, (Bmpip)2PbxSn1–xBr4 (0 < x < 1) exhibits double-peaked emission at 470 and 670 nm. The emission color of (Bmpip)2PbxSn1–xBr4 can be easily tuned from orange-red to blue by adjusting the Pb/Sn molar ratio or excitation wavelength. Representatively, (Bmpip)2Pb0.16Sn0.84Br4 exhibits approximately white-light emission with high photoluminescence quantum yield up to 39%. Interestingly, the color of (Bmpip)2PbxSn1–xBr4 can also be easily tuned by temperature, promising its potential for application in temperature measurement and indication. Phosphor-converted light-emitting diodes are fabricated by combining (Bmpip)2PbxSn1–xBr4 and 365 nm near-UV LED chips and exhibit high-quality light output.